94/6
A lead free, free-flowing solder that can be used with most ferrous and non-ferrous metals, 94/6 is used widely throughout the HVACR industry. A good choice when the high heat of a brazing alloy alternative would weaken the base metals significantly. Similar to 96/4 with better ability to fill large gaps; this alloy is of particular use where fit up is less than ideal.
Specifications
| Melting Pt. | 430 ºF 221 ºC |
| Flow Pt. | 535 ºF 279 ºC |
| MBT1 | 575 |
| AWS | Sn 94 |
| Preform Options | Bands (Sleeves) Custom Designs Discs - Coated, Cored Edgewounds Rings - Coated, Cored Washers - Coated, Cored, Linked |
| Resale Options | Bar (Various Sizes) Paste Strip - Flux Core Wire - Flux Core |
| Approx. Wire Length (BCuP/lb.) (BAg/Tr.oz) | 1203 in @ 0.062 diameter 4889 in @ 0.031 diameter 543 in @ 0.093 diameter |
Phsycial Constants
| Color | Silver |
| Density | 0.271 lb./cu.in |
Applications
A lead-free choice for applications where fit-up is less than desirable.
Downloads
Download SDS Sheet
Compare With
- AWS: Sn 94
Specifications
- Brazing Temperature Range High: 575 F / 302 C
- Brazing Temperature Range Low: 545 F / 285 C
- Liquidus: 535 F / 279 C
- Solidus: 430 F / 221 C
Composition
- Sn: 94%
- Ag: 6%
The information and recommendations contained in this publication have been provided without charge & compiled from sources believed to be reliable and to represent the best information available on the subject at the time of issue. No warranty, guarantee, or representation is made by the Prince and Izant Company, Inc. as to the absolute correctness or sufficiency of any representation contained in this and other publications; Prince and Izant Company, Inc. assumes no responsibility in connection therewith; nor can it be assumed that all acceptable safety measures are contained in this and other publications, or that other or additional measures may not be required under particular or exceptional conditions or circumstances. The company and product names referenced herein are for identification purposes only. All trademarks and registered trademarks are the property of their respective owners.